Preparation of LiMnPO4/C cathode material for lithium ion batteries by a microreactor-solid state process
Author(s):
CHEN YunchaoYU YongWANG GuojingLIU XiaominYANG Hui
College of Materials Science and Engineering,Nanjing Tech University,Nanjing 210009,China
Keywords:
microreactor solid state process Mn3(PO4)2·3H2O LiMnPO4 carbon coating
PACS:
TM911
DOI:
10.3969/j.issn.1671-7627.2017.03.004
Abstract:
Nano-sized LiMnPO4 cathode material was prepared by a microreactor-solid state method.The Mn3(PO4)2·3H2O particles,obtained by mixing two reactant solutions rapidly in a microreactor,were ball-milled with lithium and carbon sources to prepare the precursors,and the mixture was sintered under high temperatures to obtain the product LiMnPO4/C.The effects of various calcination temperatures on the particle size and electrochemical performance of LiMnPO4/C were characterized by X-ray diffraction(XRD),field emission scanning electron microscope(FESEM),transmission electron microscopy(TEM)and galvanostatic charge-discharge test.Results showed that the LiMnPO4/C calcined at 650 ℃ exhibited the smallest particle size and the best electrochemical performance.The initial discharge capacity of this sample was 121 mA·h/g at 0.05C rate(1C=171 mA·h/g),which kept the capacity retention ratio of 86.8% after 20 cycles.

References:

[1] PADHI A K,NANJUNDASWAMY K S,GOODENOUGH J B.Phospho-olivines as positive-electrode materials for rechargeable lithium batteries[J].Journal of the electrochemical society,1997,144(4):1188.
[2] HUANG Y,FANG J,O’SHEA M,et al.Understanding the stability of MnPO4[J].Journal of materials chemistry A,2014,24(32):12827.
[3] CHEN F J,TAO F,WANG C M,et al.The influence of improved carbon coating layer with nanometer-sized CeO2 interconnector on the enhanced electrochemical performance of LiMnPO4[J].Journal of power sources,2015,285(1):367.
[4] RANGAPPA D,SONE K,ZHOU Y,et al.Size and shape controlled LiMnPO4 nanocrystals by a supercritical ethanol process and their electrochemical properties[J].Journal of materials chemistry,2011,21(39):15813.
[5] ZHU H J,ZHAI W,YANG M,et al.Synthesis and characterization of LiMnPO4/C nano-composites from manganese(ii)phosphate trihydrate precipitated from a micro-channel reactor approach[J].Rsc advances,2014,4(49):25625.
[6] RAVNSBÆK D B,XIANG K,XING W,et al.Extended solid solutions and coherent transformations in nanoscale olivine cathodes[J].Nano letters,2014,14(3):1484.
[7] PARK H S,KIM T H,LEE M H,et al.Catalytic carbonization of an uncarbonizable precursor by transition metals in olivine cathode materials of lithium ion batteries[J].Journal of materials chemistry,2012,22(38):20305.
  
[8] MEMM M,KOENTJE M,AXMANN P,et al.New high-voltage step at 4.8 V in cobalt free manganese based lithium phospho olivines for lithium-ion batteries[J].Journal of power sources,2015,276(1):382.
[9] YANG X,MI Y,ZHANG W,et al.Enhanced electrochemical performance of LiFe0.6Mn0.4PO4/C cathode material prepared by ferrocene-assisted calcination process[J].Journal of power sources,2015,275(1):823.
[10] PIECZONKA N P W,LIU Z,HUQ A,et al.Comparative study of LiMnPO4/C cathodes synthesized by polyol and solid-state reaction methods for Li-ion batteries[J].Journal of power sources,2013,230(10):122.
[11] HU C L,YI H H,WANG F X,et al.Boron doping at P-site to improve electrochemical performance of LiMnPO4 as cathode for lithium ion battery[J].Journal of power sources,2014,255(6):355.
[12] 李志军,王红英,汤伟杰,等.锂离子电池正极材料LiMnPO4的制备及改性研究进展[J].电源技术,2015,39(3):616.
[13] ZHANG W,SHAN Z,ZHU K,et al.LiMnPO4 nanoplates grown via a facile surfactant-mediated solvothermal reaction for high-performance Li-ion batteries[J].Electrochimica acta,2015,153:385.
[14] 李志军,王红英,汤伟杰,等.锂离子电池正极材料LiMnPO4/C的固相法制备及性能研究[J].人工晶体学报,2015,44(3):773.

Memo

Memo:
-
Last Update: 2017-05-31