 FANG Caixiang,CAO Liangliang,YIN Wenhui,et al.Glycothermal synthesis and magnetic properties of Yb-Ce co-doped YIG nanocrystals[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2013,35(02):59-63.[doi:10.3969/j.issn.1671-7627.2013.02.012]
点击复制

Yb-Ce共掺YIG纳米晶的醇热法合成与磁性能()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
35
期数:
2013年02期
页码:
59-63
栏目:
出版日期:
2013-03-20

文章信息/Info

Title:
Glycothermal synthesis and magnetic properties of Yb-Ce co-doped YIG nanocrystals
文章编号:
1671-7627(2013)02-0059-05
作者:
方才翔曹亮亮殷文慧纪荣进曾燕伟
南京工业大学 材料科学与工程学院,江苏 南京 210009
Author(s):
FANG CaixiangCAO LiangliangYIN WenhuiJI RongjinZENG Yanwei
College of Materials Science and Engineering,Nanjing University of Technology,Nanjing 210009,China
关键词:
YIG纳米晶 Yb-Ce共掺杂 醇热法合成 磁性能
Keywords:
YIG nanocrystals Yb-Ce co-doped glycothermal synthesis magnetic properties
分类号:
TM277
DOI:
10.3969/j.issn.1671-7627.2013.02.012
文献标志码:
A
摘要:
以分散性好的钇铝石榴石(YAG)纳米晶为晶种,采用醇热法合成Yb-Ce共掺的YbxCe1.5Y1.5-xFe5O12(x=0、0.25、0.5、0.75和1.0)(YIG)纳米晶。X线衍射(XRD)测试表明各组分产物均为单相石榴石结构,经Rietveld方法全谱拟合分析发现,Yb-Ce共掺YIG纳米晶晶胞参数a不随Yb3+掺杂量的改变而显著变化(均略大于1.249 nm),平均晶粒尺寸约为30 nm,与场发射扫描电子显微镜(FESEM)观察到的颗粒尺寸一致。振动样品磁强计(VSM)测试结果表明,随Yb3+掺杂量x的增大,室温饱和磁化强度σs有所下降,这是由于Yb3+取代石榴石结构中Y3+,进入十二面体位置使晶胞分子磁矩减小所致。此外,Yb-Ce共掺YIG纳米晶饱和磁化强度与其晶粒尺寸随Yb掺杂量的变化规律呈现出一定的相似性。
Abstract:
YbxCe1.5Y1.5-xFe5O12 (YbCe-YIG)garnet nanocrystals with Yb content x=0,0.25,0.5,0.75,and 1.0 were synthesized by a glycothermal method using Y3Al5O12(YAG)nano-sized crystallites as seeds.The X-ray diffraction(XRD)analyses by Rietveld refinements showed that all synthetic products with different doping content x were single garnet phases with a cell parameter of about 1.249 nm and the mean grain size of YbCe-YIG nanocrystals was about 30 nm,it was consistent with the observation of field emission scanning electron microscopy(FESEM).Their room temperature saturation magnetization σs tested by vibrating sample magnetometer(VSM)was found to decrease with the increase of x,indicating the reduction of molecular magnetic moment due to the substitution of Yb3+ ions for Y3+ ions in dodecahedral sites.Besides,the saturation magnetization and the grain size of Yb-Ce co-doped YIG nanocrystals showed similar variations with the increase of Yb content x.

参考文献/References:

[1] Gomi M,Satoh K,Abe M.Giant Faraday rotation of Ce-substituted YIG films of epitaxially grown by RF sputtering[J].Japanese Journal of Applied Physics,1988,27(8):L1536-L1538.
[2] Toshihiro M,Takehiko U,Morio K.Magneto-optic channel waveguides in Ce-substituted yttrium iron garnet[J].Journal of Applied Physics,1993,74(8):4877-4881.
[3] Sekhar M C,Hwang J Y,Ferrera M,et al.Strong enhancement of the Faraday rotation in Ce and Bi comodified epitaxial iron garnet thin films[J].Applied Physics Letters,2009,94(18):181916.
[4] Huang M,Zhang S Y.Growth and characterization of cerium-substituted yttrium iron garnet single crystals for magneto-optical applications[J].Applied Physics A:Materials Science and Processing,2002,74(2):177-180.
[5] Xu H T,Yang H,Xu W,et al.Magnetic properties of Ce,Gd-substituted yttrium iron garnet ferrite powders fabricated using a sol-gel method[J].Journal of Materials Processing Technology,2008,197(1/2/3):296-300.
[6] Park M B,Cho N H.Structural and magnetic characteristics of yttrium iron garnet(YIG,Ce:YIG)films prepared by RF magnetron sputter techniques[J].Journal of Magnetism and Magnetic Materials,2001,231(2/3):253-264.
[7] Honda Y,Hibiya T,Shiroki K.DyBi garnet films with improvement temperature dependence of Faraday rotation[J].Journal of the Magnetics Society of Japan,1986,10(2):151-154.
[8] Booth R C,White E A D.Magneto-optic properties of rare-earth iron garnet crystals in the wavelength range 1.1-1.7 μm and their use in device of fabrication[J].Journal of Physics D:Applied Physics,1984,17:579-587.
[9] Huang M,Zhang S Y,Wu H X.Faraday rotation effects of(HoYbBi)3Fe5O12 single crystal and its application to wideband and temperature-stabilized optical isolators[J].Physica Status Solidi(a),1997,163(1):255-261.
[10] Huang M,Zhang S Y.Structural,magnetic and magneto-optical properties of(YYbBi)3Fe5O12 single crystal for high-performance magneto-optical applications[J].Physica Status Solidi(a),2001,185(2):487-492.
[11] Xu Z C,Huang M,Li M.A compounded rare-earth iron garnet single crystal exhibiting stable Faraday rotation against wavelength and temperature variation in the 1.55 μm band[J].Journal of Magnetism and Magnetic Materials,2006,307(1):74-76.
[12] Grosseau P,Bachiorrini A,Guilhot B.Preparation of polycrystalline yttrium iron garnet ceramics[J].Power Technology,1997,13:247-251.
[13] Vaqueiro P,Crosnier-Lopez M P,López-Quintela M A.Synthesis and characterization of yttrium iron garnet nanoparticles[J].Journal of Solid State Chemistry,1996,126:161-168.
[14] Wu L,Yu J C,Zhang L Z,et al.Selective self-propagating combustion synthesis of hexagonal and orthorhombic nanocrystalline yttrium iron oxide[J].Journal of Solid State Chemistry,2004,177:3666-3674.
[15] Inoue M,Nishikawa T,Nakamura T,et al.Glycothermal reaction of rare-earth acetate and iron acetylacetonate:formation of hexagonal ReFeO3[J].Journal of the American Ceramic Society,1997,80(8):2157-2160.
[16] Inoue M,Otsu H,Kominami H,et al.Glycothermal synthesis of rare earth aluminium garnets[J].Journal of Alloys and Compounds,1995,226(1/2):146-151.
[17] Noda K,Asakura R,Isobe T,et al.Glycothermal synthesis and magnetic properties of YIG/YAG nanoparticles[J].Advances in Nanomaterials and Processing,2007,126:863-866.
[18] Toby B H.EXPGUI,a graphical user interface for GSAS[J].Journal of Applied Crystallography,2001,34:210-213.
[19] Sánchez R D,Rivas J,Vaqueiro P,et al.Particle size effects on magnetic properties of yttrium iron garnets prepared by a sol-gel method[J].Journal of Magnetism and Magnetic Materials,2002,247(1):92-98.
[20] Rajendrana M,Dekab S,Joyb P A,et al.Size-dependent magnetic properties of nanocrystalline yttrium iron garnet powders[J].Journal of Magnetism and Magnetic Materials,2006,301(1):212-219.

备注/Memo

备注/Memo:
收稿日期:2012-03-31
基金项目:江苏省高校自然科学基金重点项目(06KJA43008)
作者简介:方才翔(1985—),男,湖北赤壁人,硕士,主要研究方向为磁性功能材料; 曾燕伟(联系人),教授,E-mail: zengyanwei@tom.com..
更新日期/Last Update: 2013-03-31