[1]刘开伟,邓敏,莫立武,等.Na2SO4侵蚀下粉煤灰对砂浆开裂的抑制作用[J].南京工业大学学报(自然科学版),2014,36(04):34-38.[doi:10.3969/j.issn.1671-7627.2014.04.007]
 LIU Kaiwei,DENG Min,MO Liwu,et al.Inhibition of fly ash on cracking of mortars immersed in sodium sulfate solution[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2014,36(04):34-38.[doi:10.3969/j.issn.1671-7627.2014.04.007]
点击复制

Na2SO4侵蚀下粉煤灰对砂浆开裂的抑制作用()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
36
期数:
2014年04期
页码:
34-38
栏目:
出版日期:
2014-07-01

文章信息/Info

Title:
Inhibition of fly ash on cracking of mortars immersed in sodium sulfate solution
文章编号:
1671-7627(2014)04-0034-05
作者:
刘开伟邓敏莫立武黄蓓
南京工业大学 材料科学与工程学院 材料化学工程国家重点实验室,江苏 南京 210009
Author(s):
LIU KaiweiDENG MinMO LiwuHUANG Bei
State Key Laboratory of Materials-Oriented Chemical Engineering,College of Materials Science and Engineering,Nanjing Tech University,Nanjing 210009,China
关键词:
硫酸盐侵蚀 无损检测 粉煤灰 钙钒石
Keywords:
sulfate attack non-destructive testing fly ash ettringite formation
分类号:
TU528
DOI:
10.3969/j.issn.1671-7627.2014.04.007
文献标志码:
A
摘要:
将不同粉煤灰掺量的砂浆浸泡在5% Na2SO4溶液中养护,利用表面观察和超声波测试等无损测试技术跟踪浸泡过程中砂浆表面裂纹和内部裂纹的变化,通过热分析对侵蚀产物相进行分析,并采用激光共聚焦显微镜(LSCM)和扫描电子显微镜(SEM)对浸泡360 d的样品进行内部微观结构分析。结果表明:钙钒石是导致开裂的主要原因,掺入粉煤灰能够提高砂浆的抗渗性、阻止外部SO2-4的持续侵入,减少钙钒石的生成从而抑制砂浆表面和内部裂纹的形成,且粉煤灰掺量越高抑制效果越明显。
Abstract:
The mortars,prepared with various contents of fly ash,were immersed in 5% Na2SO4 solutions.Non-destructive testing,surface observation and ultrasonic test were used to track the changes of the surface cracks and the inner cracks of mortars attacked by sodium sulfate solution.Thermal analysis was used to identify the compounds and laser scanning confocal microscope(LSCM)and scanning electron microscope(SEM)were used to examine the microstructure of the mortars immersed in 5% Na2SO4 solution for 360 days.Results showed that the formation of ettringite was responsible for cracking, and the incorporation of fly ash could reduce the permeability and prevent the sulfate ingress.The surface and inner cracks were reduced by reducing the amount of ettringite, thus the effect was better with the increase of the dosages of fly ash.

参考文献/References:

[1] Neville A.The confused world of sulfate attack on concrete [J].Cement and Concrete Research,2004,34(8):1275-1296.
[2] 邢志水.工程混凝土硫酸盐侵蚀破坏调查与分析 [D].南京:南京工业大学,2012.
[3] 王复生,孙瑞莲.察尔汗盐湖条件下水泥混凝土耐久性调查研究[J].硅酸盐通报,2002,21(4):16-22.
[4] Skalny J,Marchand J,Odler I.Sulfate attack on concrete [M].London:Spon Press,2002.
[5] Müllauer W,Beddoe R E,Heinz D.Sulfate attack expansion mechanisms [J].Cement and Concrete Research,2013,52:208-215.
[6] 袁晓露,周明凯,李北星.混凝土抗硫酸盐侵蚀性能的测试与评价方法综述 [J].混凝土,2008(2):12.
[7] Komlos K,Popovics S,Nürnbergerova T,et al.Ultrasonic pulse velocity test of concrete properties as specified in various standards [J].Cement and Concrete Composites,1996,18(5):357-364.
[8] Torrent R J.A two-chamber vacuum cell for measuring the coefficient of permeability to air of the concrete cover on site[J].Materials and Structures,1992,25(6):358-365.
[9] Wang J G.Sulfate attack on hardened cement paste [J].Cement and Concrete Research,1994,24(4):735-742.
[10] Chen J,Jiang M.Long-term evolution of delayed ettringite and gypsum in Portland cement mortars under sulfate erosion [J].Construction and Building Materials,2009,23(2):812-816.
[11] Chabrelie A.Mechanisms of degradation of concrete by external sulfate ions under laboratory and field conditions [D].Lausanne:École Polytechnique Fédérale de Lausanne,2010.
[12] Mather B.Discussion of “the process of sulfate attack on cement mortars” by Shen Yang,Xu Zhongzi,Tang Mingshu[J].Advanced Cement Based Materials,1997,5(3):109-110.
[13] Santhanam M.Studies on sulfate attack:mechanisms,test methods,and modeling [D].Lafayette:Purdue University,2001.
[14] Sakai E,Miyahara S,Ohsawa S,et al.Hydration of fly ash cement[J].Cement and Concrete Research,2005,35(6):1135-1140.

相似文献/References:

[1]张旭苹.超声换能器压电陶瓷材料的选择[J].南京工业大学学报(自然科学版),1991,13(02):80.

备注/Memo

备注/Memo:
收稿日期:2014-01-13
基金项目:江苏省普通高校研究生科研创新计划(CXZZ12_0414)
作者简介:刘开伟(1985—),男,江苏扬州人,博士生,主要研究方向为水泥混凝土; 邓敏(联系人),教授,E-mail:dengmin@njtech.edu.cn..
更新日期/Last Update: 2014-07-31