[1]许彦明,徐玲玲,李文伟.XRD内标法测定高镁水泥熟料中方镁石含量和水化程度[J].南京工业大学学报(自然科学版),2014,36(05):30-35.[doi:10.3969/j.issn.1671-7627.2014.05.006]
 XU Yanming,XU Lingling,LI Wenwei.Quantitative determination of periclase and periclase hydration in high magnesium cement clinker with XRD internal standard method[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2014,36(05):30-35.[doi:10.3969/j.issn.1671-7627.2014.05.006]
点击复制

XRD内标法测定高镁水泥熟料中方镁石含量和水化程度()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
36
期数:
2014年05期
页码:
30-35
栏目:
出版日期:
2014-09-30

文章信息/Info

Title:
Quantitative determination of periclase and periclase hydration in high magnesium cement clinker with XRD internal standard method
文章编号:
1671-7627(2014)05-0030-06
作者:
许彦明1徐玲玲1李文伟2
1.南京工业大学 材料科学与工程学院,江苏 南京 210009; 2.中国长江三峡集团公司,湖北 宜昌 443002
Author(s):
XU Yanming1XU Lingling1LI Wenwei2
1.College of Materials Science and Engineering,Nanjing Tech University,Nanjing 210009,China; 2.China Three Gorges Corporation,Yichang 443002,China
关键词:
高镁熟料 XRD内标法 方镁石 膨胀
Keywords:
high magnesium cement clinker XRD internal standard method periclase expansion
分类号:
TQ172.1
DOI:
10.3969/j.issn.1671-7627.2014.05.006
文献标志码:
A
摘要:
采用X线衍射(XRD)内标法,以ZnO作为内标物对高镁水泥水化浆体中方镁石进行定量分析,并利用回收率评价其准确性。观察方镁石水化膨胀对浆体试块产生的破坏情况,并利用扫描电子显微镜(SEM)观察140 d方镁石水化产物的形貌。结果表明:内标法可以用于定量测定高镁水泥浆体中的方镁石含量并根据测定结果确定方镁石的水化程度。在30 ℃养护180 d时方镁石水化程度为46.66%,在80 ℃养护60 d时方镁石的水化程度为86.39%,180 d时达到90.64%,水化趋于完全。SEM观察发现,80 ℃水化140 d时方镁石颗粒表面有片状水镁石形成。80 ℃养护条件下,高镁熟料中方镁石水化60 d产生的膨胀对水泥试块产生破坏作用,而养护温度低于38 ℃时方镁石水化缓慢,水化140 d的高镁水泥浆体试块没有明显的外观变化。
Abstract:
A quantitative X-ray diffractometic(XRD)method with ZnO as an internal standard was used for estimating periclase and brucite in high-magnesia cement paste.Recovery was used to evaluate the accuracy.Periclase hydration expansion resulting in slurry block damaging was investegated.The appearance of 140 d periclase hydration was analyzed by scanning electron microscopy(SEM).Results showed that XRD internal standard method could be used for the determination of periclase and study the degree of periclase hydration in high magnesium cement paste.The degree of periclase hydration was 46.66% in 180 d under 30 ℃, and it was 86.39% in 60 d and was 90.64% in 180 d under 80 ℃.It was found that the laminate brucite appeared on periclase surface in 140 d under 80 ℃ by SEM. The expansion of periclase hydration resulted in cement block damaging in 60 d under 80 ℃.Periclase hydration was very slow at the temperature lower than 38 ℃,and the influence of slurry block damaging was not significant in 140 d.

参考文献/References:

[1] 张大同,陈萍,赵福欣,等.关于水泥中方镁石危害性及其检测方法的研究现状与问题[J].中国建筑材料科学研究院学报,1990,2(4):72-78.
[2] 李广才.水泥水化系统中Ca(OH)2的热重定量测定研究及应用[J].硅酸盐通报,1986(5):52-57.
[3] 廖绍峰,陈阳显,李化建.X射线衍射定量分析在水泥熟料分析中的应用[J].建材技术与应用,2004(6):11-13.
[4] 杨南如.无机非金属测量方法[M].武汉:武汉理工大学出版社,2005:23-25.
[5] 单小兵,张其土,李玉华.X衍射K值法在水泥物相中的应用[J].理化检验:物理分册,2002,38(8):342-345.
[6] 陈福松,徐玲玲,张志宾.水泥熟料中方镁石定量分析[J].硅酸盐通报,2009,28(6):1295-1299,1305.
[7] 洪汉烈,赵曼曲.水泥熟料X射线定量物相分析方法的对比研究[J].分析仪器,2001(2):21-23.
[8] 李玉华.用X射线K值法定量分析水泥物相[J].水泥工程,2001(3):34-38.
[9] 洪汉烈,陈建军,杨淑珍,等.水泥熟料定量分析的全谱拟合法[J].分析测试学报,2001,20(2):5-8.
[10] Rehsi S S,Majumdar A J.Quantitative determination of uncombined MgO in Portland cement clinker by X-Ray diffractometry[J].Journal of Applied Chemistry,1968,18:297-300.
[11] 杨淑珍,周和平.无机非金属材料测试实验[M].武汉:武汉工业大学出版社,1997:18-20.

备注/Memo

备注/Memo:
收稿日期:2013-10-23
基金项目:国家科技支撑计划(2011BAE27B01)
作者简介:许彦明(1986—),男,江苏宿迁人,硕士生,主要研究方向为无机非金属材料; 徐玲玲(联系人),教授,E-mail:xulingling1964@163.com..
更新日期/Last Update: 2014-09-20