[1]杨思晟,凌祥,陆树华.热损伤后材料力学性能的小冲孔试验分析[J].南京工业大学学报(自然科学版),2016,38(01):45-49.[doi:10.3969/j.issn.1671-7627.2016.01.008]
 YANG Sisheng,LING Xiang,LU Shuhua.Mechanical properties analysis of materials with thermal damage by small punch test[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2016,38(01):45-49.[doi:10.3969/j.issn.1671-7627.2016.01.008]
点击复制

热损伤后材料力学性能的小冲孔试验分析()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
38
期数:
2016年01期
页码:
45-49
栏目:
出版日期:
2016-01-10

文章信息/Info

Title:
Mechanical properties analysis of materials with thermal damage by small punch test
文章编号:
1671-7627(2016)01-0045-05
作者:
杨思晟凌祥陆树华
南京工业大学 机械与动力工程学院,江苏 南京 211800
Author(s):
YANG SishengLING XiangLU Shuhua
College of Mechanical and Power Engineering,Nanjing Tech University,Nanjing 211800,China
关键词:
小冲孔试验 热损伤 力学性能
Keywords:
small punch test thermal damage mechanical properties
分类号:
TG113.25
DOI:
10.3969/j.issn.1671-7627.2016.01.008
文献标志码:
A
摘要:
基于小冲孔试验技术建立载荷-位移曲线中弹塑性转变温度、最大载荷、断裂位移与材料屈服强度、抗拉强度、断后延伸率之间的关联,从而分析不同热损伤条件下304不锈钢以及Q345R钢的力学性能变化。结果表明:相比于新材料,不同损伤参数下材料力学性能发生明显变化并可以使用小冲孔试验进行合理分析。随着损伤时间的延长,2种材料的屈服强度和抗拉强度均会出现一定程度下降,而在热损伤12 h后304不锈钢的抗拉强度基本不变。损伤时间达到48 h时,损伤温度的提高将会导致材料屈服强度和抗拉强度的明显下降。304不锈钢的断后延伸率随着损伤温度的升高逐步增加,而Q345R钢的断后延伸率则存在一定的分散性。
Abstract:
To analyze the mechanical properties of materials under different thermal damage conditions,three important parameters were obtained from the load-displacement(L-D)curves based on small punch test for the elastic plastic transition load,maximum load and fracture displacement.Results showed that property evolutions could be accurately estimated by small punch test.There was a significant change of mechanical properties under different thermal damage conditions.With the increase of damage time,the yield strength and the ultimate tensile strength would decrease. The degradation of ultimate tensile strength would become unapparent when damage time was more than 12 h.Meanwhile,the increase of the damage temperature would result in the decrease of the yield strength and the ultimate tensile strength when damage time reached 48 h.The fracture displacement analysis indicated that tensile elongation of 304 stainless steel would increase with higher temperature,while the change of the ultimate tensile strength of Q345R was not evident.

参考文献/References:

[1] 杨景标,陈学东,范志超,等.07MnNiMoDR钢火灾后力学性能及组织研究:拉伸性能[J].压力容器,2014,31(3):1.
[2] HYDE T H,SUN W,WILLIAMS J A.Requirements for and use of miniature test specimens to provide mechanical and creep properties of materials:a review[J].International materials reviews,2007,52(4):213.
[3] 钟巍华,佟振峰,张长义,等.小冲杆测试辐照对反应堆压力容器钢力学性能的影响[J].金属学报,2011,47(9):1205.
[4] SERRE I,VOGT J B.Liquid metal embrittlement of T91 martensitic steel evidenced by small punch test[J].Nuclear engineering and design,2007,237(7):677.
[5] GUAN K S,HUA L,WANG Q Q,et al.Assessment of toughness in long term service CrMo low alloy steel by fracture toughness and small punch test[J].Nuclear engineering and design,2011,241(5):1407.
[6] 凌祥,周志祥,解巧云.小冲孔试验技术研究及其应用[J].南京工业大学学报(自然科学版)2009,31(2):106.
[7] RODRÍGUEZ C,CARCÍA CABEZAS J,CÁRDENAS E,et al.Mechanical properties characterization of heat-affected zone using the small punch test[J].Welding journal,2009,88:188.
[8] RUAN Y,SPÄTIG P,VICTORIA M.Assessment of mechanical properties of the martensitic steel EUROFER97 by means of punch tests[J].Journal of nuclear materials,2002,307-311:236.
[9] FINARELLI D,ROEDIG M,CARSUGHI F.Small punch tests on austenitic and martensitic steels irradiated in a spallation environment with 530 MeV protons[J].Journal of nuclear materials,2004,328(2/3):146.
[10] GARCÍA T E,RODRÍGUEZ C,BELZUNCE F J,et al.Estimation of the mechanical properties of metallic materials by means of the small punch test[J].Journal of alloys and compounds,2014,582:708.
[11] TURBA K,GÜLCIMEN B,LI Y Z,et al.Introduction of a new notched specimen geometry to determine fracture properties by small punch testing[J].Engineering fracture mechanics,2011,78(16):2826.
[12] 徐鹏.压力容器用钢16MnR高温损伤后应变疲劳特性研究[D].杭州:浙江大学,2006.

相似文献/References:

[1]凌 祥,周志祥,解巧云.小冲孔试验技术研究及其应用[J].南京工业大学学报(自然科学版),2009,31(02):106.
 LING Xiang,ZHOU Zhiliang,XIE Qiaoyun.Research and application on small punch test technology[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2009,31(01):106.
[2]凌祥,胡若美.R60702锆材小冲孔蠕变特性[J].南京工业大学学报(自然科学版),2009,31(05):1.
 LING Xiang,HU Ruo mei.Small punch creep characteristics of R60702 Zirconium[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2009,31(01):1.

备注/Memo

备注/Memo:
收稿日期:2014-12-12
基金项目:国家高技术研究发展计划(863计划)(2012AA040105); 江苏省普通高校研究生科研创新计划(KYZZ15_0229)
作者简介:杨思晟(1989—),男,江苏东台人,博士生,主要研究方向为微试样试验技术与高温蠕变损伤研究; 凌祥(联系人),教授,E-mail:xling@njtech.edu.cn.
引用本文:杨思晟,凌祥,陆树华.热损伤后材料力学性能的小冲孔试验分析[J].南京工业大学学报(自然科学版),2016,38(1):45-49..
更新日期/Last Update: 2016-01-20