 WANG Jing,LI Weixing,XING Weihong.Vapor permeation enhanced esterification of acetic acid and isopropanol by CS-PVA/PVDF composite membrane[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2015,37(02):7-11.
点击复制

CS-PVA/PVDF膜蒸汽渗透强化乙酸异丙醇的酯化反应()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
37
期数:
2015年02期
页码:
7-11
栏目:
出版日期:
2015-03-20

文章信息/Info

Title:
Vapor permeation enhanced esterification of acetic acid and isopropanol by CS-PVA/PVDF composite membrane
作者:
王 静李卫星邢卫红
(南京工业大学 材料化学工程国家重点实验室,江苏 南京210009)
Author(s):

WANG JingLI WeixingXING Weihong

(State Key Laboratory of Materials-Oriented Chemical Engineering, Nanjing Tech University, Nanjing 210009, China)

关键词:
CS-PVA/PVDF乙酸异丙醇蒸汽渗透
Keywords:
chitosan-poly (vinyl alcohol)/polyvinylidene fluoride (CS-PVA/PVDF) acetic acid isopropanol vapor permeation
文献标志码:
A
摘要:
将实验室制备的壳聚糖-聚乙烯醇/聚偏氟乙烯(CS-PVA/PVDF)中空纤维复合膜,用于蒸汽渗透耦合乙酸异丙醇酯化反应。通过扫描电子显微镜(SEM) 表征膜的微观结构。研究了复合膜在蒸汽渗透下分离水/异丙醇的性能。考察了耦合酯化反应过程中反应温度、催化剂用量、醇酸初始摩尔比以及膜温对酯产率和膜通量的影响。结果表明:膜分离层与支撑体结合紧密;复合膜对水/异丙醇体系具有较好的分离性能。酯化反应的最佳条件:反应温度95 ℃,醇酸摩尔比2.5:1,催化剂用量3%,膜温90 ℃。在最佳条件下,反应11.5 h,酯收率由非耦合时的82.7%提高到耦合时的99.2%。
Abstract:
Abstract: The hollow fiber composite membrane chitosan-poly (vinyl alcohol)/polyvinylidene fluoride (CS-PVA/PVDF) was prepared and applied in esterification of acetic acid and isopropanol coupled with vapor permeation (VP). The microstructure of the membrane was characterized by scanning electron microscope (SEM) and the separation performance of membrane was investigated. Effects of various operating conditions including reaction temperature, catalyst loading, initial molar ratio of acetic acid to isopropanol and membrane temperature were considered. Results indicated that the separation layers were successfully coated onto the supports and the membrane exhibited high efficiency in separating water from water/isopropanol mixture. The optimized conditions were reaction temperature of 95 ℃, initial molar ratio of acetic acid to isopropanol of 1:2.5, catalyst loading of 3 wt% and membrane temperature of 90 ℃. Under the optimized conditions, the yield of isopropyl acetate increased from 82.7% to 99.2% with VP at 11.5 h.

相似文献/References:

[1]李有林,崔咪芬,乔旭,等.乙酸和丙烯一步合成乙酸异丙酯工艺[J].南京工业大学学报(自然科学版),2010,32(03):30.
 LI Youlin,CUI Mifen,QIAO Xu,et al.Technology of one-step synthesis of isopropyl acetate by acetic acid and propylene[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2010,32(02):30.
[2]陈曦,王俊,韩越,等.超声辅助SiW12/SiO2催化合成乙酸苄酯及动力学[J].南京工业大学学报(自然科学版),2011,33(04):24.[doi:10.3969/j.issn.1671-7627.2011.04.006]
 CHEN Xi,WANG Jun,HAN Yue,et al.Ultrasound assisted heteropoly acid catalyst SiW12/SiO2 for synthesis of benzyl acetate and kinetics[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2011,33(02):24.[doi:10.3969/j.issn.1671-7627.2011.04.006]
[3]崔咪芬,乔旭,王龙恩,等.乙酸光氯化制备氯乙酸的反应动力学[J].南京工业大学学报(自然科学版),2002,24(02):24.[doi:10.3969/j.issn.1671-7627.2002.02.006]
[4]张媛,乔旭,崔咪芬,等.乙酸光氯化合成三氯乙酸宏观动力学研究[J].南京工业大学学报(自然科学版),2006,28(01):80.[doi:10.3969/j.issn.1671-7627.2006.01.018]
 ZHANG Yuan,QIAO Xu,CUI Mi-fen,et al.Kinetics of the synthesis of trichloroacetic acid by photo-chlorination of acetic acid[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2006,28(02):80.[doi:10.3969/j.issn.1671-7627.2006.01.018]
[5]王静,李卫星,邢卫红.CS-PVA/PVDF膜蒸汽渗透强化乙酸异丙醇的酯化反应[J].南京工业大学学报(自然科学版),2015,37(02):45.[doi:10.3969/j.issn.1671-7627.2015.02.009]
 WANG Jing,LI Weixing,XING Weihong.Vapor permeation enhanced esterification of acetic acid and isopropanol by CS-PVA/PVDF composite membrane[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2015,37(02):45.[doi:10.3969/j.issn.1671-7627.2015.02.009]

备注/Memo

备注/Memo:
?收稿日期:2014-02-20

基金项目:国家科技支撑计划(2013BAE11B01);江苏省高校自然科学研究计划(11KJB530005)

作者简介:王 静(1988—),女,江苏扬州人,硕士,主要研究方向为膜分离;李卫星(联系人),教授,E-mail:wxli@njtech.edu.cn.

更新日期/Last Update: 2014-12-18